Polymer Journal 4 – Reflection

Prototype #1:

By mixing Super Slime and Boogers together, we made our first prototype called “Super Booger”. It was very stretchy and gel-like without being too sticky or wet. It seemed perfect for our design goal. One thing I would change was that even though it seemed simple to make with just two base polymers, it took a lot of extra materials to perfect and adjust it to how we wanted. This polymer was unique but hard to create.

Prototype #2:

Our second prototype called “Super Everything” attempted to combine Gloop, Boogers, Super Slime and Oobleck together. The result was stretchy and gel-like just like our first prototype, but it was sticky and was very wet as we had added a large amount of water for the Oobleck. In the end, it was too sticky and hard to clean to be a polymer that was meant to keep things together without damaging them.



We performed a few tests on Prototype #1 to see if it was really that strong. It was poked slowly and quickly to see if any of it would stick to a surface. The polymer only left the object wet for a few seconds and none of it was displaced. It was stretched extremely long and held in the air at the sides to see how long it could go without breaking. It stretched for over ten meters and did not collapse to pressure. It was dropped at around a one-meter height and bounced instead of splattering across the table.

Our first prototype is the most effective at performing its intended purpose. Since our goal was to create a polymer that holds things together like a piece of string or an elastic band, Prototype #1 proved to be much stronger. Both prototypes were fairly stretchy and gel-like, although the first prototype was much less slime-like and held its form better. Its non-sticky and dry properties made it superior to its alternative, due to the polymer’s ease of use and cleanliness.

If we had more time allocated for us to work on this product, I would try to find a way to make it less wet, as even though it left no stains or damage, it visibly left a mark when placed on the table.

I believe we did fairly well in these steps of the design process; however, two prototypes may not be enough. If we had more time to create more than two different types of polymers, we would have had a more complete and finalized product. Our prototypes should have also been tested and observed more, to see the strengths and weaknesses of each design.

Here are the steps to create our polymer, “Untangled Slime”:

  1. Measure 55g of glue in a cup.
  2. Measure 40mL of PVA solution in a graduated cylinder and pour into a separate cup.
  3. Measure 40mL of laundry starch in a graduated cylinder.
  4. Measure 8mL of borax solution in another graduated cylinder.
  5. Pour the borax into the cup with the PVA solution and stir for a few minutes while mixing the laundry starch with the glue, stirring both simultaneously.
  6. Combine the two polymers together in a large beaker, adding around 5mL of borax to the mixture if necessary to help the two polymers mix.
  7. Pick up the mixture and mold it until the two polymers have visually combined into one.

Polymer Journal 3 – How Will We Make It?

What will the polymer be like?

Physical properties of our polymer include:

  • Elasticity

The polymer should not break very easily when stretched very wide or pressed down with a moderate amount of force. Otherwise, it would not be useful to hold anything together.

  • Not sticky and not wet

No one likes an incredibly sticky or wet slime. It gets everywhere – on clothing, on desks, on the skin – and is hard to get off. A sticky polymer would not be useful for our design either.

  • Bouncy

A bouncy polymer will feel less slimy and will stick to fewer surfaces. It will also be less likely to break when dropped. All of these characteristics are ideal for a moldable rope-like design that we are going for.

  • Aesthetically pleasing

Who doesn’t like something that looks good?


How are we going to build our prototypes?

Created using draw.io

How will the polymer be tested?

After the creating stage is completed, the polymer will be stuck to surfaces, wrapped around small objects, pushed on, poked, molded, and stretched into a long, thin strand. It will also be left out overnight to dry. These tests are to ensure that the polymer fulfills (or does not fulfill) the desired physical properties. A good prototype should be maintaining these properties.

Polymer Journal 2 – What is it For?

The polymer that I (we) want to design is for a very specific situation but could potentially be helpful.

It will be similar to this design, protecting the wire from being broken and also holding it together to prevent the earbuds from tangling. The targeted audience is, if not obvious enough, people who use earbuds, namely people who experience the problem of untangling earbuds that have unfortunately been coiled together several times in their pockets.

This polymer will hold earbuds in a neat position, making them a lot easier to unravel.

The relative lack of stickiness in Gloop makes any polymer with this characteristic ideal for attaching to items. I also liked the simplicity of Super Slime, which consists of only two materials. Adding more of one material would make the substance more watery and less solid, adding more of the other would make it thicker and drip less liquid.

Polymer Journal 1 – Natural vs. Synthetic Materials


Lazonby, John. “Ethene (Ethylene).” The Essential Chemical Industry Online, www.essentialchemicalindustry.org/chemicals/ethene.html.

“How Is Nylon Made?” OpenLearn, The Open University, 26 Sept. 2005, www.open.edu/openlearn/science-maths-technology/science/chemistry/how-nylon-made.

“Natural vs. Synthetic Polymers.” Gelfand Center – Carnegie Mellon University, www.cmu.edu/gelfand/education/k12-teachers/polymers/natural-synthetic-polymers/.

“Polyester.” How Products Are Made, www.madehow.com/Volume-2/Polyester.html.